CLT-Classical-Laminate-Theory-Failure-Prediction
Predicition of Laminate Failure using Classical Laminate Theory (CLT)
The Tsai-Hill criterion is a quadratic, interactive stress-based criterion that identifies failure, but does not distinguish between different modes of failure.
Failure occurs whenever the following condition is satisfied.
The coefficients Sij of the Tsai-Hill criterion are computed as follows:
S+11 = Value of σ11 at longitudinal tensile failure
S-11 = Value of σ11 at longitudinal compressive failure
S+22= Value of σ22 at transverse tensile failure
S-22 = Value of σ22 at transverse compressive failure
S12 = Absolute value of σ12 at longitudinal shear failure